Materials Matter: Gear Surfaces and Operational Performance

Machined Surfaces

The term machining can be applied to a multitude of techniques, each with unique properties and characteristics. However, all such techniques require a tool that is strong and/or sharp enough to cut into the surface in a predefined manner. To achieve a cutting action, the technique employed must overcome the physical strength of the metal, which results in the generation of a large amount of heat. This force and heat affects the stress-strain relationship and causes the fracture and flow of metal, leading to the creation of the Beilby layer [2]. Plastic deformation of the metal during machining results in cold working of the surface and the creation of the worked layer. These physical alterations to the surface have the effect of increasing the hardness and tensile stresses while decreasing ductility and reducing performance values. Because the stress and strain exerted on the component is high, discontinuous micro-cracks form [3]. In addition to these physical property changes, all machining operations produce “peak asperities” that reduce the effective contact areas of the component.

Isotropic Superfinished Surfaces
As described in the October “Materials Matter” column, an isotropically superfinished surface will possess a surface roughness of <0.25 µm and a non-directional surface texture. Through the use of isotropic superfinishing in the form of chemically accelerated vibratory finishing, the distressed material layer (the Beilby layer and the uppermost portions of the worked layer) can be completely removed, leaving behind a layer of homogenous material, free from the defects inherent to a machined surface. These surface improvements are possible due to the nature of the chemically accelerated vibratory finishing process — namely, that it is carried out at ambient temperatures and requires exceptionally little force. These factors dictate that no detrimental physical property alterations will occur during the material removal process.

Operating Properties of Machined vs. Isotropic Superfinished Surfaces
The surface of a gear is the point of contact between two mating surfaces, and the contacting properties will be derived directly from the interaction of these two mating surfaces. (See Figure 2.)

With machined surfaces, the unfavorable properties of the surface material itself and the peak asperities serve as initiating factors for surface fatigue during operation via the progression of micropitting or abrasive wear.

An isotropically superfinished surface, no longer having any micro-cracks or surface distress (tensile stress) and possessing a planarized texture, will not suffer from either of these failure modes. In fact, the surface’s contact properties now resemble that of Hertzian contact theory, as the two contacting bodies are, in essence, flat. This characteristic allows the surfaces to distribute the load over the whole theoretical contact area, diminishing the contact pressure across the active flank and significantly improving the component’s resistance to contact fatigue.

The Importance of Texture
It is important to note that the texture of an isotropic superfinish is critical, as a surface that is free of all texture is, in fact, too smooth. A non-textured or “too smooth” surface struggles to retain adequate lubrication during operation and is therefore at a greater risk for scuffing or galling damage. The machined surface shown in Figure 3 will fail well before the surfaces shown in Figure 4 and Figure 5 in any contact fatigue testing for these reasons. However, despite both surfaces having no peak asperities of distressed metal flaws, the surface shown in Figure 4 has been shown to outperform the surface shown in Figure 5 by a considerable degree in scuffing tests due to its more favorable lubricant retention properties despite the surface in Figure 5 having a lower coefficient of friction.

Getting the Optimal Surface
In conclusion, it is clear that the surface of a gear is a key factor in its operational performance. To achieve maximum performance, it is beneficial to remove the distressed material that is generated during the machining process(es). It is also critical to planarize the surface while making sure that you retain an adequate level of texture for optimal lubricant retention during loaded operation (this is how REM’s ISF® Process functions). The importance of the surface to a gear’s operational performance and the ability to accurately evaluate or verify these desired surface characteristics in production is clear. To this end, the next part of this series will discuss the methods of measuring and evaluating surfaces and surface roughness in order to avoid misconceptions or errant classifications.


  1. Astakhov, V.P. (2010). Surface integrity — Definition and importance in functional performance. In J.P. Davim (Ed.), Surface Integrity in Machining, (pp. 1-35). London: Springer-Verlag.
  2. Abukhshim, N. A., & Mativenga, P. T., & Shiekh, M.A. (2005). Heat generation and temperature prediction in metal cutting: A review and implications for high speed machining, International Journal of Machine Tools & Manufacture, Vol. 46 (Issues 7-8), pp. 782-800.
  3. Shaw, M.C. (2003). The size effect in metal cutting, Sadhana, Vol. 28, Issue 5, pp. 875-896.


Justin Michaudis the vice president of REM Surface Engineering, a leader in the metal finishing industry for over 50 years. Michaud’s expertise is in lean manufacturing, operational and financial management, and strategic planning. He is a graduate of the University of Notre Dame’s Mendoza College of Business where he was a member of the university’s men’s soccer team.

This article first appeared in December 2015 edition of Gear Solutions Magazine.  To view more on this Gear Solutions article, please click here.

Download Resource

Please fill out the information below to receive the selected resource.

Download Resource New Form

Please fill out the information below to receive the selected resource.